*PONENT
|
RESULT
|
|
|
1
|
ASH CONTENT, NOT MORE THAN %
|
0.14
|
|
2
|
MASS FRACTION OF SULPHUR, NOT MORE THAN %
-LOW – SULPHUR – RESIDUE - OIL
|
<0.5%
|
|
3
|
TEMPERATURE OF THE FLASH, NOT LESS THAN DEGREE’S C IN THE CLOSED CRUCIBLE
|
>65
|
|
IN THE OPEN CRUCIBLE
|
>110
|
|
|
4
|
THE TEMPERATURE OF SOLIDIFICATION, NOT HIGHER
THAN DEGREE’S C
|
25
|
|
5
|
KINEMATICS VISCOSITY
|
118 MAX
|
|
6
|
WATER CONTENT
|
0.5%
|
|
7
|
MECHANICAL IMPURITIES
|
LOWER THAN 0.1%
|
|
8
|
ACIDITY
|
LOWER THAN 0.5 KOH/100ML
|
|
9
|
ALKALINITY
|
NIL
|
|
10
|
GROSS CALORIFIC VALUE KCAL/KG / KJ/KG
|
MIN 9700 / 41300
|
|
11
|
DENSITY AT 15.0 DEG C KG/L
|
0.8900 – 0.9200
|
|
12
|
HYDROGEN SULFIDE CONTENT (H2S) POM
|
0.5 MAX
|
|
13
|
CARBON RESIDUE
|
LOWER THAN 7%
|
|
14
|
VANADIUM (V) PPM
|
23
|
|
15
|
ALUMINUM (AL) PPM
|
5
|
|
16
|
SILICON (SL) PPM
|
12
|
|
17
|
NICKEL (NI) PPM
|
29 or 49
|
|
18
|
ASPHALTENES
|
3.6%
|
|
19
|
DISTILLATION @ 4MM HG
|
|
|
EXTRACTED TO 760 MM HG
|
||
|
INITIAL BOILING POINT DEG. C
|
216
|
|
|
5% RECOVERED DEG C
|
259
|
|
|
10% RECOVERED DEG C
|
310
|
|
|
20% RECOVERED DEG C
|
358
|
|
|
30% RECOVERED DEG C
|
445
|
|
|
40% RECOVERED DEG C
|
502
|
|
|
50% RECOVERED DEG C
|
534
|
|
|
60% RECOVERED DEG C
|
538
|
|
|
75% RECOVERED DEG C
|
545
|
|
|
80% RECOVERED DEG C
|
-
|
|
|
90% RECOVERED DEG C
|
-
|
|
|
FINAL BOILING POINT DEG C
|
550
|
|
|
PERCENT RECOVERED VOL
|
78%
|
|
|
RESIDUE VOL
|
22%
|
|
|
TOTAL NITROGEN M/M
|
0.192%
|
|
|
20
|
SODIUM (NA) PPM
|
15
|