羅地亞PA6 TECHNYL C 216 V30 產(chǎn)品特性：含30%玻璃纖維增強(qiáng)，潤滑，熱性能和機(jī)械性能的良好結(jié)合，用于汽車，電子電氣應(yīng)用等
我公司提供的產(chǎn)品均為正牌塑膠原料，品質(zhì)保證，貨源穩(wěn)定，送貨上門，可免費(fèi)提供官方物性表、UL黃卡，并隨貨提供RoHS報告、SGS報告等，索取權(quán)威資料請致電13268582149
PA6 C216V30 物性表：
| Physical | Dry | Conditioned | Unit | Test Method |
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Density | 1350 | -- | kg/m³ | ISO 1183 2 |
| Water Absorption (23°C, 24 hr) | 0.95 | -- | % | ISO 62 |
| Water Absorption (Equilibrium) | 2.1 | -- | % | ISO 62 2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
| Tensile Modulus | 9600 | 6200 | MPa | ISO 527-2/1A |
| Tensile modulus | 9600 | 6200 | MPa | ISO 527-2 2 |
| Tensile Stress (Break) | 190 | 110 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 190 | 110 | MPa | ISO 527-2 2 |
| Tensile Strain (Break) | 3.8 | 4.5 | % | ISO 527-2/1A |
| Tensile Strain (Break) | 3.8 | 4.5 | % | ISO 527-2 2 |
| Flexural Modulus | 9500 | 5500 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
| Charpy Notched Impact Strength | 15 | 32 | kJ/m² | ISO 179/1eA |
| Charpy notched impact strength (23°C) | 15.0 | 31.5 | kJ/m² | ISO 179/1eA 2 |
| Charpy Unnotched Impact Strength | 100 | 110 | kJ/m² | ISO 179/1eU |
| Charpy impact strength (23°C) | 100 | 108 | kJ/m² | ISO 179/1eU 2 |
| Notched Izod Impact Strength | 14 | 24 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
| Deflection Temperature Under Load (0.45 MPa) | 217 | -- | °C | ISO 75-2 2 |
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | -- | °C | ISO 75-2/Af |
| Deflection Temperature Under Load (1.8 MPa) | 205 | -- | °C | ISO 75-2 2 |
| Glass Transition Temperature 3 | 55 | -- | °C | ISO 11357-2 2 |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 3146 |
| Melting Temperature 3 | 222 | -- | °C | ISO 11357-3 2 |
| CLTE - Flow | 0.000032 | -- | cm/cm/°C | ISO 11359-2 2 |
| CLTE - Transverse (23 to 85°C) | 0.000032 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Surface resistivity | -- | 1.0E+11 | ohms | IEC 60093 2 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohm·cm | IEC 60093 |
| Volume resistivity | 1.0E+13 | 1.0E+9 | ohm·m | IEC 60093 2 |
| Relative Permittivity (1 MHz) | 3.80 | 4.50 | IEC 60250 2 | |
| Dissipation Factor | 0.020 | 0.090 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.090 | IEC 60250 2 | |
| Comparative Tracking Index (Solution A) | 550 | 475 | V | IEC 60112 |